Panasonic Corp. has achieved the world’s highest energy conversion efficiency for a perovskite solar module at 16.09% using a glass substrate and a large-area coating method based on inkjet printing. This was carried out as part of the project of the New Energy and Industrial Technology Development Organization (NEDO).
This inkjet-based coating method that can cover a large area reduces manufacturing costs of modules (aperture area here is 802 cm2: 30 cm long x 30 cm wide x 2 mm thick). In addition, this large-area, lightweight, and high-conversion efficiency module allows for generating solar power highly efficiently at locations where conventional solar panels were difficult to install, such as façades.
Going forward, NEDO and Panasonic continue to improve perovskite layer materials, aiming to achieve high efficiency comparable to that of crystalline silicon solar cells and establish technologies for practical application in new markets.
What’s the deal with perovskite again?
Perovskite solar cells have a structural advantage because their thickness including a power generation layer is only one-hundredth of that of crystalline silicon solar cells, so that perovskite modules can be lighter in weight than crystalline silicon modules. The lightweight property enables various placing styles such as installing on façades and windows by using transparent conductive electrode, which can lead to the wide-spread adoption of Net Zero Energy Buildings.
Further, as each layer can be coated onto the substrates directly, they can be produced cheaper, compared to the conventional process technology. That is why perovskite solar cells are getting attention as next generation solar cells.
On the other hand, despite perovskite technology achieved 25.2% power conversion efficiency, comparable to crystalline silicon solar cells, in small size cells, it was very difficult to deposit materials uniformly all over large-area by conventional technology. As a result, the power conversion efficiency was inclined to decrease.
The inkjet method
By focusing on the inkjet coating method that enables the raw material to be coated precisely and uniformly, Panasonic applied that technology to each layer of the solar cell including perovskite layer on glass substrate and realized high power conversion efficiency for a large-area module.
Among the atomic groups that formed perovskite crystal, methylamine has thermal stability issue during the heating process during module production (methylamine is removed from perovskite crystal by heat, as a result, a certain part of crystal is destroyed). By altering certain part of methylamine into Formamidinium, Cesium, Rubidium that have appropriate atom diameter size, they revealed this method is efficient for crystal stabilization and leads to contribute to high power conversion efficiency.
[button link=”https://staging1.solarbuildermag.com/category/residential-solar/” window=”yes”]February is Operations & Maintenance Month here at Solar Builder. Check out all of our O&M news and insights this month right here.[/button]
In the thin film forming process with inkjet coating method, there is the flexibility for coating pattern, while dot patterning of material and crystallization uniformity over each layer surface are essential. To satisfy these requirements, both by tuning the concentration of perovskite ink to certain content and by precisely controlling coating amount and speed during printing process, they realized high power conversion efficiency of large-area module.
By optimizing these technologies through coating process in each layer formation, Panasonic succeeded in enhancing crystal growth and improving the uniformity for thickness and crystal layer. As a result, they achieved the power conversion efficiency of 16.09% and took a step forward to practical application.
By realizing lower process cost and more lightweight for a large-area perovskite module, NEDO and Panasonic Corporation will plan to create new market in which the solar cells have never been placed and adopted. Based on development of each material related to perovskite solar cells, NEDO and Panasonic aim to achieve high efficiency comparable to that of crystalline silicon solar cells and enhance the effort to reduce producing cost to 15 yen/W.
Listen to more in-depth conversations on Solar Builder's YouTube channel
Our most popular series include:
Power Forward! | A collaboration with BayWa r.e. to discuss higher level industry topics.
The Buzz | Where we give our 2 cents per kWh on the residential solar market.
The Pitch | Discussions with solar manufacturers about their new technology and ideas.